LOGICROOF P-RP FB
Polyester reinforced TPO/FPA membrane for single-ply waterproofing of exposed flat roofs bonded on the lower face with nonwoven polyester fabric.
Synthetic waterproofing membrane produced by co-extruding a UV resistant elastomerised TPO/FPA thermoplastic olefin and flexible polypropylene alloy, with a polyester net reinforcement bonded on the lower face with nonwoven polyester fabric. The membrane features contrasting colours on its upper and lower faces, providing a signal layer so that any damage occurring during or after installation will be immediately apparent. Available in BIANCO REFLECTA version, manufactured with the upper side of the membrane (top) in WHITE REFLECTA colour, by means of a treatment developed in mass in the entire layer that covers the top of the reinforcement. This process enhances the reflectance and emission features giving the roof a Solar Reflectance Index (SRI) value that reach 102%. LOGICROOF P-RP FB membranes comply with CE marking requirements, if applicable.
Fields of application
Specific use
- Mechanically retained waterproofing on exposed roofs.
- Waterproofing layers applied independently under heavy-duty fixed or movable protection for:
- roofing exposed to foot traffic;
- inverted roofs.
TECHNICAL FEATURES (1)
| Features | EN Standards | U.M. | Tolerance | Values | |||
|---|---|---|---|---|---|---|---|
| Standard thickness | 1849-2 | mm | (-5/+10%) | 1,2 | 1,5 | 1,8 | 2,0 |
| Tensile properties | |||||||
| Tensile strength L/T | 12311-2 | N/50 mm | 1100 / 1100 | ||||
| Elongation at break L/T | 12311-2 | % | 25 / 25 | ||||
| Dimensional stability | 1107-2 | % | ≤ 0.5 / 0.5 | ||||
| Cold flexibility | 495/5 | °C | ≤ -40 (2) | ||||
| Tear resistance L/T | 12310/1 | N | 550 / 650 (*) | ||||
| Water vapour permeability (resistance factor μ) | 1931 | 50.000 | |||||
| Resistance to static loading | 12730/B | kg | ≥ 25 (*) | ||||
| Resistance to impact | 12691/B | mm | ≥ 1800 (*) | ||||
| Hail resistance | 13583 | m/s | ≥ 30 (3) | ||||
| Water tightness (60 kPa) | 1928 | Absolute | |||||
| Joint strength | |||||||
| Tensile strength | 12317-2 | N/cm | Compliant (specimen fails outside bond area) | ||||
| Peeling | 12316-2 | N/cm | ≥ 58 | ||||
| Durability | |||||||
| Resistance to artificial UV light | 1297-5000 h | No surface damage or significant changes in cold flexibility as per EN 495/5 | |||||
| Heat aging in area | |||||||
| Change in tensile strength | 12311-2 | Δ% | -5 | ||||
| Change in elongation at break | 12311-2 | Δ% | -5 | ||||
| Reaction to fire | 13501-1 | Class F | |||||
| Resistance to algae and microorganisms | ISO 846 Level 2 | Compliant | |||||
| Root resistance | 13948 | Passes the test | |||||
Notes:
(1) Tolerances as per EN 13956 and/or UEAtc Directives.
(*) The values indicated refer to the TPO / FPA membrane without nonwoven polyester fabric backing, except for the values marked with an
asterisk (*), that refer to the finished product.
(2) Not tested at lower temperatures.
(3) Not tested at higher speeds
PRODUCTION STANDARDS
| Thickness (*) | mm | 1,2 | 1,5 | 1,8 | 2,0 |
| Width | m | 2,10 | 2,10 | 2,10 | 2,10 |
| Length (*) | m | 25 | 25 | 20 | 20 |
| Standard colour (*) | Grey / Black | ||||
(*) Different thicknesses, lengths and colours are available on demand and for minimum quantities